产品特点
①包装：20kg/桶或25kg/桶;
②白色粉体，斑点率低，应用良品率高;
③适配干压成型、等静压成型、注射成型、流延成型、凝胶成型、热压注成型、3D打印等多种成型工艺，流动性好，生坯成型性能好;
④产品烧结性能好，易烧结，收缩比稳定，烧结收缩一致性好;
⑤烧结体机械性能优异，强度、硬度和韧性较高;
⑥适用于生产大型结构陶瓷，也适用于生产小微精密陶瓷部件;
应用领域
①结构陶瓷及各种规格陶瓷异形件;
②研磨设备陶瓷部件以及其他耐磨陶瓷;
③氧化锆研磨介质(锆珠);
④陶瓷餐刀;
⑤智能穿戴产品、陶瓷手表配件和陶瓷饰品等;
⑥复合材料添加剂;
⑦光纤插芯、套管等光通讯陶瓷;
⑧纺织、理发器用陶瓷刀片;
⑨半导体及医疗用陶瓷部件;
⑩阀门、柱塞等流体设备陶瓷部件;
型号参数
| 参数项目ITEM | 规 格 MODEL | |||||
| ZC-3YB-W1 | ZC-3YB-W2 | ZC-3YB-W3 | ZC-3YB-W4 | ZC-3YB-W5 | ||
| 化学成分(wt%) Chemical Component | Zr(Hf)O2 | ≥94.0 | ≥94.0 | ≥94.2 | ≥94.2 | ≥94.2 |
| Y2O3 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | |
| Al2O3 | 0.25±0.02 | 0.25±0.02 | ﹤0.01 | ﹤0.01 | ﹤0.01 | |
| Fe2O3 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| SiO2 | ﹤0.02 | ﹤0.02 | ﹤0.02 | ﹤0.02 | ﹤0.02 | |
| TiO2 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| Na2O | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| 水分Water Composition(wt%) | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | |
| 灼减L.O.I(wt%) | ﹤3.0 | ﹤3.0 | ﹤3.0 | ﹤3.0 | ﹤3.0 | |
| 粒径D50(μm) | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤0.3 | |
| 松装密度Bulk Density(g/cm3) | 1.0-1.5 | 1.0-1.5 | 1.0-1.5 | 1.0-1.5 | 1.0-1.5 | |
| 比表面积SURFACE AREA(m2/g) | 6～10 | 10～12 | 12～16 | 20～25 | 12～16 | |
| 参数项目ITEM | 规 格 MODEL | |||||
| ZC-3YN-W1/R | ZC-3YN-W2/R | ZC-3YN-W3/R | ZC-3YN-W4 | ZC-3YN-W5 | ||
| 化学成分(wt%) Chemical Component | Zr(Hf)O2 | ≥94.0 | ≥94.2 | ≥94.0 | ≥94.2 | ≥94.2 |
| Y2O3 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | 5.25±0.25 | |
| Al2O3 | 0.25±0.02 | 0.25±0.02 | 0.25±0.02 | ﹤0.01 | 5±0.2 | |
| Fe2O3 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| SiO2 | ﹤0.02 | ﹤0.02 | ﹤0.02 | ﹤0.02 | ﹤0.02 | |
| TiO2 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| Na2O | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | ﹤0.005 | |
| 水分Water Composition(wt%) | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | |
| 灼减L.O.I(wt%) | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | ﹤1.0 | |
| 粒径D50(μm) | ﹤1.0 | ﹤0.5 | ﹤1.0 | ﹤0.2 | ﹤0.1 | |
| 松装密度Bulk Density(g/cm3) | 1.0-1.5/-- | 1.0-1.4/-- | 1.0-1.5/-- | 1.0-1.5 | 1.0-1.3 | |
| 比表面积SURFACE AREA(m2/g) | 6～10 | 6～10 | 12～16 | 14～18 | 6～12 | |