3N5隔膜氧化铝技术指标:
产品型号 | UG-L900 | UG-L800 | UG-L600 | ||
Al2O3(纯度) | % | ≥99.95 | ≥99.95 | ≥99.95 | |
杂质含量(%) | Si | (ppm)< | 200 | 200 | 200 |
Fe | 80 | 80 | 80 | ||
Na | 200 | 200 | 200 | ||
Ca | 20 | 20 | 20 | ||
H2O | % | ≤0.15 | ≤0.15 | ≤0.1 | |
BET | m2/g | 4-6 | 5-7 | 8-10 | |
ph值 | 7.0-8.5 | 7.0-8.5 | 7.0-8.5 | ||
粒度 | D10 | μm | 0.5-0.6 | 0.4-0.5 | 0.3-0.4 |
D50 | 0.9-1.2 | 0.7-0.9 | 0.5-0.7 | ||
D90 | 1.5-2.0 | 1.2-1.5 | 0.8-1.2 | ||
D100 | <4 | <2 | <2 | ||
可根据客户要求调整粒度 | |||||
外观 | 白色粉末,粉体无结块,无异物 | ||||
晶相 | a相 |
4N5隔膜氧化铝技术指标:
产品型号 | UG-L900N | UG-L800N | UG-L600N | ||
Al2O3(纯度) | % | ≥99.995 | ≥99.995 | ≥99.995 | |
杂质含量(%) | Si | (ppm)< | 30 | 30 | 30 |
Fe | 20 | 20 | 20 | ||
Na | 20 | 20 | 20 | ||
Ca | 20 | 20 | 20 | ||
H2O | % | ≤0.15 | ≤0.15 | ≤0.1 | |
BET | m2/g | 4-6 | 5-7 | 8-10 | |
ph值 | 7.0-8.5 | 7.0-8.5 | 7.0-8.5 | ||
粒度 | D10 | μm | 0.5-0.6 | 0.4-0.5 | 0.3-0.4 |
D50 | 0.9-1.2 | 0.7-0.9 | 0.5-0.7 | ||
D90 | 1.5-2.0 | 1.2-1.5 | 0.8-1.2 | ||
D100 | <4 | <2 | <2 | ||
可根据客户要求调整粒度 | |||||
外观 | 白色粉末,粉体无结块,无异物 | ||||
晶相 | a相 |
高纯氧化铝在锂电池隔膜涂层方面的技术应用优势:
优势一:
电流过大时,能够阻断电流。PP/PE材料的锂电池隔膜是通孔,当电流过大时,很容易造成穿孔现象,进而造成锂电池燃烧或者爆炸,而用高纯氧化铝作为涂层材料与粘合剂一起使用涂覆在PP/PE材料表面可以起到调孔的作用,这是因为高纯氧化铝为板状晶体结构,当电流过大时,材料发热,进而板状晶体结构的高纯氧化铝涂层材料就会体积膨胀,就会闭合锂电池隔膜上的电流传导孔,从而起到阻断电流的作用,当温度降下来时,材料体积会收缩,这时隔膜上的电流传导孔就会重新打开,利用该材料特殊的物理和化学性能,可以大大提高锂电池的性能,从而为大功率锂电池高能量可靠充放电提供了可能。
优势二:
高纯氧化铝还具有非常优良的导热性能,电池温度过高里,这种材料可以很好地进行热量传导,从而解决了PP/PE材料导热性差的问题。
优势三:
高纯氧化铝材料还具有优良的阻燃性,这是因为高纯氧化铝材料本身就是非常优良的阻燃剂,即使因为温度过高,达到燃烧零界点点,该材料的良好的阻燃性能会阻止大范围的燃烧甚至爆炸。
应用特性:
1纳米氧化铝用作锂电池电极涂层,可以有效的起到隔热,绝缘的作用。
2纳米氧化铝应用于改性进尖晶石锰酸锂材料,生产出的电池可逆容量达到107mAh/克,55C循环200次, 容量保持率大于90%,可用于高功率锂离子电池的材料。
3随着锂离子充电电池容量的不断提高,内部蓄积的能量越来越大,内部温度会提高,有可能出现温度过高使负极隔膜被融化而造成短路;如果在隔膜上涂上一层纳米氧化铝涂层,就能避免电极之间短路。
使用方法:粉体需搅拌研磨成分散液,按一定的比例做成涂料,用涂布机涂到锂电池隔膜上;液体可直接用涂布机涂到隔膜上,涂层厚度一般在2-3um。
储存方法:密封保存,置于阴凉干燥处存放。